Multi CR HS 2:1

Acrylic clear coat

Variants

ColourArt. No.Capacity Quantity per carton
transparent103471 l6
transparent98645 l4
Hardener for clear coat
standard13983 0,5 l6
standard139842,5 l4
fast10348 0,5 l6
fast98652,5 l4

Gloss grade

high gloss
Multi CR HS 2:1

Technical documentation

Weight/Volume Calculator

mlg
Primer
Hardener:00
Total of mixture00
Minimum thinner0%00
Total of mixture00
Maximum thinner0%00
Total of mixture00
Thinner value %00
Warning: Value is not within the tolerance given by the manufacturer. (Min: , Max: ).
Total of mixture00

Video

Description

High quality 2K acrylic clearcoat for quick car repairs with low content of volatile compounds and increased scratch resistance (SR).  The use of latest generation of raw materials allows the achievement of very short drying time, speeding up the repair process- painted panel is ready for installation within 2 hours after the application has been completed using the fast hardener.

Advantages

  • High resin content.
  • Short drying time.
  • Very high gloss
  • Excellent surface look.
  • Easy application.

Substrates

Acrylic clear coats can be applied over:

  • Base coats.
  • Old finishes in good condition after matting and degreasing.

For dulling the color we recommend the following :

  • grey abrasive cloth with matting compound.
  • sanding paper with gradation of 600÷800 (for dulling on wet).
  • sanding paper with gradation of  360÷500 (for dulling by machine).

Important informations

  • Przetrzeć odtłuścić

    degrease

  • Proporcje mieszania

    Mixing ratio
    2 : 1 + 0÷5%  stand.
    2 : 1 + 10%  fast

  • Lepkość natryskowa

    Spray viscosity
    15 ÷ 17 sec / 20°C

  • Żywotność mieszanki

    Pot life
    4 h / 20°C  standard
    3 h / 20°C  fast

  • Liczba warstw

    2 full layers
    HVLP / RP
    1,3 ÷ 1,4 mm

  • Czas odparowania

    between layers
    approx. 5÷7 min

  • Czas odparowania

    before baking
    approx. 10 min

  • Czas utwardzania

    Hardening time
    15 min / 60°C
    3h / 20°C standard
    2h / 20°C fast

Application process

  • Zastosowanie
  • Use

    Quick repair of the car bodies that require a durable finish.

  • Proporcje mieszania
  • Mixing ratio by volume

    Clear Coat: 2
    Hardener: 1
    Thinner:

    • with standard hardener 0-5%
    • with fast hardener 10%

    *the use of accelerating agents and express thinners are not recommended.

  • Lepkość natryskowa
  • Spraying viscosity

    15÷17 seconds at 20°C DIN4

  • Żywotność mieszanki
  • Pot life for the mixture

    standard hardener: 4 hours
    fast hardener: 3 hours

  • Liczba warstw
  • Gun parameters

    2 layers: 2 full layers, total dry film thickness of 50÷60 μm.
    RP nozzle: 1.3÷1.4mm; Pressure of input: 2.0÷2.2 bars.
    HVLP nozzle: 1.3÷1.4mm; Inlet pressure: 2.0 bars.

    Note: Follow the gun producer’s recommendations.

  • Czas odparowania
  • Evaporation time

    Between layers: aprox. 5÷7 min
    Before baking: 10 min

    *flash oof time depends on the type of painting booth

  • Czas utwardzania
  • Hardening time

    At 20°C
    Dust dry: 30 min
    Touch free: 2h fast or 3h standard hardener
    Hardness to use: 8h fast or 10h standard hardener
    Total hardness: 7 days

    At 60°C
    Dust dry: 10 min
    Touch free: 15 min
    Hardness to use: 15 min + 3 h. / 20°C
    Total hardness: 15 min + 3 days / 20°C

    Temperature below 20oC significantly increases the hardening time.

  • Suszenie promieniem IR
  • IR Drying

    10 ÷ 15 minutes under short waves, depending on the layer thickness and the type of radiator. Do not exceed 60°C. Use as recommended by the equipment manufacturer. Wait about 10 minutes before starting the IR drying.

  • Informacja
  • Product efficiency

    1 liter of mixture is enough to cover approx. 8÷10 m2 of dry layer with thickness of 60 μm.

  • Informacja
  • Shading

    Make sure you have covered the whole area with the base coat and do the shading only on a previously prepared area. Use FADE OUT THINNER to blend the dust that has settled around the repaired surface and to eliminate optical gloss differences between the old lacquer and the newly applied acrylic clear coat.

  • Informacja
  • Polishing and removing inclusions

    Usually polishing is unnecessary as MULTI CR HS 2:1 gives the surface a perfect look immediately after application. If there are any impurity inclusions, it is recommended to remove them and afterwards polish with a polishing compound.

  • Informacja
  • General notes
    • Do not exceed recommended doses of hardener!
    • The best repair results can be achieved when application is done at room temperature. Temperature in body shop and the product temperature should be the same.
    • When working with 2K products, it is recommended to use personal protection equipment. Protect the eyes and air ways.
    • The rooms should be well ventilated.
    • Tools should be cleaned immediately after use.