MS 2:1

Acrylic clear coat

Variants

ColourArt. No.Capacity Quantity per carton
transparent101581 l6
transparent83935 l4
Hardener for clear coat
standard10159 0,5 l6
standard83952,5 l4
fast154080,5 l6
fast92472,5 l4
slow154090,5 l6
slow154102,5 l4

Gloss grade

high gloss
MS 2:1

Technical documentation

Weight/Volume Calculator

mlg
Primer
Hardener:00
Total of mixture00
Minimum thinner0%00
Total of mixture00
Maximum thinner0%00
Total of mixture00
Thinner value %00
Warning: Value is not within the tolerance given by the manufacturer. (Min: , Max: ).
Total of mixture00

Video

Description

High quality bicomponent acrylic clear coat with high gloss and increased resistance SR (Scratch Resistant). Designed for quick spot repairs and complete car body painting.

Advantages

  • Very good flow.
  • High gloss.
  • Hard and durable coating.
  • High Scratch resistance.
  • Universal use.

Substrates

MS Acryl Clear Coat 2:1 can be applied over:

  • Base coats.
  • Old finishes in good condition after matting and degreasing.

Important informations

  • Przetrzeć odtłuścić

    degrease

  • Proporcje mieszania

    Mixing ratio
    2 : 1 + 0÷3%

  • Lepkość natryskowa

    Spray viscosity
    15 ÷ 16s / 20°C

  • Żywotność mieszanki

    Pot life
    5 h / 20°C

  • Liczba warstw

    2 full layers
    HVLP / RP
    ø1,3 ÷ 1,4 mm

  • Czas odparowania

    between layers
    approx. 5 min.

  • Czas odparowania

    before baking
    approx. 10 min.

  • Czas utwardzania

    Hardening time
    30 min. / 20°C
    30 min. / 60°C
    (for standard hardener)

  • Suszenie promieniem IR

    15÷20 min.

Application process

  • Zastosowanie
  • Use

    For car body repairs that require a durable finish.

  • Proporcje mieszania
  • Mixing ratio by volume

    Clear Coat: 2
    Hardener: 1
    Thinner: 0÷3%

  • Lepkość natryskowa
  • Spraying viscosity

    15÷16 seconds at 20°C.

  • Żywotność mieszanki
  • Pot life

    Approx. 5 hours at 20°C.

  • Liczba warstw
  • Number of layers

    2 full coats, 50÷70 µm of dry film for each layer
    RP gun Parameters
    Nozzle: 1.3÷1.4 mm; Pressure: 2,0÷2,2 bar.
    HVLP gun Parameters
    Nozzle: 1.3÷1.4 mm; Pressure inside the nozzle: 2,0 bar.

  • Czas odparowania
  • Evaporation time

    Between layers: about 5 minutes
    Before baking: about 10 minutes

  • Czas utwardzania
  • Curing time

    At 20°C
    Dust free: about 30 minutes.
    Ready to polish: after drying overnight.

    At 60°C
    Clear coat is ready to polish after baking for about 30 minutes and cooling down (about 2 hours).

    Temperature below 20°significantly increases the drying time.

  • Suszenie promieniem IR
  • Drying with IR radiator

    15÷20 minutes of short waves, depends from the type of the machine
    Do not exceed the temperature of 60°C.
    Follow the producer instructions.
    Wait about 10 minutes before drying with IR radiator.