Ultra Fast Drying HS 2:1

Acrylic clearcoat

Variants

ColourArt. No.Capacity Quantity per box
transparent2010 0,5 l6
transparent19621 l6
Hardener for clearcoat
standard5944 0,25 l6
standard14770,5 l6

Gloss grade

high gloss
Ultra Fast Drying HS 2:1

Technical documentation

Weight/Volume Calculator

mlg
Primer
Hardener:00
Total of mixture00
Minimum thinner0%00
Total of mixture00
Maximum thinner0%00
Total of mixture00
Thinner value %00
Warning: Value is not within the tolerance given by the manufacturer. (Min: , Max: ).
Total of mixture00

Video

Description

ULTRA FAST DRYING is an acrylic clearcoat with increased SR (Scratch Resistant).Extremely short hardening time makes it ideal for smart quick repairs. Painted element is ready for installation within 90 min. after application, without baking!

PERFORMANCE: 1 liter of the mixture is enough to paint 10,5 m2 of surface with a a thickness layer of 60 μm.

Advantages

  • Short drying time.
  • Easy application.
  • Excellent overspray absorption.
  • Very good fluidity.
  • High hardeness and glossy finish.
  • Increased resistance to scratches SR (scratch resistant).

Substrates

Acrylic clearcoats can be applied over:

  • Basecoats.
  • Old paint coatings in good condition after matting and degreasing.

Important informations

  • Przetrzeć odtłuścić

    degrease

  • Proporcje mieszania

    Mixing ratio
    2 : 1

  • Lepkość natryskowa

    Spraying viscosity
    16 ÷ 17s / 20°C

  • Żywotność mieszanki

    Pot life
    60 min. / 20°C

  • Liczba warstw

    2 layers
    HVLP / RP
    ø1,2 ÷ 1,4 mm

  • Czas odparowania

    between layers
    8 ÷ 10 min.

  • Czas utwardzania

    Drying time
    90 min. / 20°C

Application process

  • Zastosowanie
  • Use

    Fast car body repairs that required durable finish.

  • Proporcje mieszania
  • Mixing proportion per volume

    Clearcoat: 2
    Hardener: 1
    Thinner: max. 0%

  • Lepkość natryskowa
  • Spraying viscosity

    16÷17 seconds at 20ºC

  • Żywotność mieszanki
  • Pot life for the mixture

    60 minutes at 20ºC

  • Liczba warstw
  • Number of layers

    2 full layers; about 50-60 µm of dry coating.
    RP gun parameters
    Nozzle: 1,2÷1,4mm; Pressure: 2,0÷2,2 bar.
    HVLP gun parameters
    Nozzle: 1,3÷1,4mm; Inlet pressure: 2,0 bar.

    Caution: Follow the recommendations of the equipment manufacturer.

  • Czas odparowania
  • Flash off time

    Between layers: about 8÷10 min.

  • Czas utwardzania
  • Drying time

    Dust dry: 30 min / 20ºC.
    Ready to use: 90 min / 20ºC and relative humidity not exceeding 80%.

    * Temperatures below 20°C significantly increase the drying time.

  • Suszenie promieniem IR
  • IR Drying

    10÷15 minutes under short wave depending on the total thickness and type of radiator.
    Do not exceed maximum temperature of 60°C.
    Use according to the recommendations of the equipment manufacturer.
    Wait about 10 minutes before starting IR drying.

  • Informacja
  • Performance

    1 liter of the mixture is enough to paint 10,5 m2 of surface with a layer thickness of 60 μm.

  • Informacja
  • Polishing and eliminating defects

    Usually polishing is unnecessary, as the C18 VHS Clear Coat 2:1 gives the surface a perfect finish immediately after application. However, if some dirt inclusions appear, we recommend removing them and then polishing the surface with an abrasive compound.

  • Informacja
  • General notes
    • Do not exceed recommended doses of the hardener!
    • The best repair results can be achieved by painting at room temperature. The temperature in the body shop and the temperature of the product should be similar. When working with 2K products, it is recommended to use personal protection equipment. Protect the eyes and airways.
    • The rooms should be well ventilated.
    • Clean the guns and equipment immediately after use.

    Caution: To maintain safety, always follow the instructions given in the MSDS for the products.